PA 6/12 vs. LDPE
Both PA 6/12 and LDPE are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is PA 6/12 and the bottom bar is LDPE.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.7 to 2.2 | |
| 0.3 |
| Tensile Strength: Ultimate (UTS), MPa | 40 to 58 | |
| 7.0 |
Thermal Properties
| Maximum Temperature: Decomposition, °C | 450 | |
| 400 |
| Melting Onset (Solidus), °C | 210 | |
| 110 |
| Specific Heat Capacity, J/kg-K | 1590 | |
| 2300 |
| Thermal Conductivity, W/m-K | 0.22 | |
| 0.36 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 3.9 to 12 | |
| 2.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.1 | |
| 0.92 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.89 to 1.2 | |
| 0.18 |
| Stiffness to Weight: Bending, points | 38 to 41 | |
| 24 |
| Strength to Weight: Axial, points | 10 to 15 | |
| 2.1 |
| Strength to Weight: Bending, points | 25 to 31 | |
| 8.8 |
| Thermal Diffusivity, mm2/s | 0.13 | |
| 0.17 |