PA 6/6 vs. PPE
Both PA 6/6 and PPE are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is PA 6/6 and the bottom bar is PPE.
Metric UnitsUS Customary Units
Material Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 3.0 to 4.3 | |
| 2.7 |
| Dielectric Strength (Breakdown Potential), kV/mm | 25 to 30 | |
| 19 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.6 to 23 | |
| 2.3 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 to 13 | |
| 13 |
| Elongation at Break, % | 2.8 to 46 | |
| 30 |
| Flexural Strength, MPa | 80 to 260 | |
| 75 |
| Glass Transition Temperature, °C | 50 | |
| 85 |
| Maximum Temperature: Autoignition, °C | 460 | |
| 430 |
| Melting Onset (Solidus), °C | 260 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 60 to 240 | |
| 55 |