PA 6 vs. PP Copolymer
Both PA 6 and PP copolymer are thermoplastics. There are 7 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is PA 6 and the bottom bar is PP copolymer.
Metric UnitsUS Customary Units
Material Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 10 to 30 | |
| 21 to 22 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.1 to 16 | |
| 0.9 to 1.1 |
| Elongation at Break, % | 2.5 to 67 | |
| 12 |
| Flexural Modulus, GPa | 1.2 to 14 | |
| 1.3 |
| Flexural Strength, MPa | 40 to 230 | |
| 31 |
| Melting Onset (Solidus), °C | 230 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 35 to 210 | |
| 23 to 33 |