PBT vs. PAR
Both PBT and PAR are thermoplastics. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is PBT and the bottom bar is PAR.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.7 to 8.7 | |
| 2.0 |
| Elongation at Break, % | 2.5 to 43 | |
| 50 |
| Flexural Modulus, GPa | 2.6 to 9.1 | |
| 2.1 |
| Flexural Strength, MPa | 79 to 210 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 58 to 140 | |
| 67 |
Thermal Properties
| Glass Transition Temperature, °C | 40 | |
| 190 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 4.0 | |
| 170 |
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 160 | |
| 180 |
| Maximum Temperature: Decomposition, °C | 380 | |
| 470 |
| Specific Heat Capacity, J/kg-K | 1040 to 1200 | |
| 1200 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 to 1.5 | |
| 1.2 |
| Limiting Oxygen Index (LOI), % | 20 | |
| 35 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.1 to 3.2 | |
| 0.93 |
| Stiffness to Weight: Bending, points | 35 to 45 | |
| 35 |
| Strength to Weight: Axial, points | 12 to 25 | |
| 16 |
| Strength to Weight: Bending, points | 25 to 38 | |
| 31 |