PC vs. PP Homopolymer
Both PC and PP homopolymer are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is PC and the bottom bar is PP homopolymer.
Metric UnitsUS Customary Units
Mechanical Properties
| Elongation at Break, % | 3.5 to 110 | |
| 3.0 to 80 |
| Flexural Modulus, GPa | 2.3 to 10 | |
| 1.5 to 7.0 |
| Flexural Strength, MPa | 92 to 160 | |
| 41 to 100 |
| Impact Strength: Notched Izod, J/m | 140 to 440 | |
| 42 to 95 |
| Tensile Strength: Ultimate (UTS), MPa | 66 to 160 | |
| 36 to 93 |
Thermal Properties
| Glass Transition Temperature, °C | 150 | |
| 170 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 130 to 150 | |
| 73 to 160 |
| Specific Heat Capacity, J/kg-K | 1000 to 1200 | |
| 1230 to 1900 |
| Thermal Expansion, µm/m-K | 10 to 69 | |
| 30 to 90 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.2 to 1.4 | |
| 0.91 to 1.2 |
| Water Absorption At Saturation, % | 0.16 to 0.19 | |
| 0.010 to 0.090 |
Common Calculations
| Strength to Weight: Axial, points | 15 to 30 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 30 to 45 | |
| 27 to 37 |