PEEK vs. DAP
PEEK belongs to the thermoplastics classification, while DAP belongs to the thermoset plastics. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is PEEK and the bottom bar is DAP.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 120 to 300 | |
| 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 to 24 | |
| 13 |
| Elongation at Break, % | 1.6 to 43 | |
| 31 |
| Flexural Strength, MPa | 150 to 330 | |
| 62 |
| Impact Strength: Notched Izod, J/m | 78 to 120 | |
| 14 |
| Tensile Strength: Ultimate (UTS), MPa | 97 to 200 | |
| 28 |
Thermal Properties
| Glass Transition Temperature, °C | 240 | |
| 150 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 160 to 300 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 1390 to 1700 | |
| 1450 |
| Thermal Conductivity, W/m-K | 0.25 to 0.93 | |
| 0.6 |
| Thermal Expansion, µm/m-K | 15 to 52 | |
| 25 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 3.0 to 14 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 to 1.5 | |
| 1.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.5 to 10 | |
| 4.1 |
| Stiffness to Weight: Bending, points | 36 to 73 | |
| 46 |
| Strength to Weight: Axial, points | 20 to 41 | |
| 4.5 |
| Strength to Weight: Bending, points | 36 to 55 | |
| 12 |
| Thermal Diffusivity, mm2/s | 0.1 to 0.51 | |
| 0.24 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 6.3 |