PEEK vs. PMP
Both PEEK and PMP are thermoplastics. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is PEEK and the bottom bar is PMP.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 to 24 | |
| 1.1 |
| Elongation at Break, % | 1.6 to 43 | |
| 30 |
| Impact Strength: Notched Izod, J/m | 78 to 120 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 97 to 200 | |
| 24 |
Thermal Properties
| Glass Transition Temperature, °C | 240 | |
| 30 |
| Maximum Temperature: Mechanical, °C | 330 | |
| 140 |
| Melting Onset (Solidus), °C | 340 | |
| 230 |
| Specific Heat Capacity, J/kg-K | 1390 to 1700 | |
| 1750 |
| Thermal Conductivity, W/m-K | 0.25 to 0.93 | |
| 0.17 |
| Thermal Expansion, µm/m-K | 15 to 52 | |
| 120 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 3.0 to 14 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 to 1.5 | |
| 0.83 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.5 to 10 | |
| 0.74 |
| Stiffness to Weight: Bending, points | 36 to 73 | |
| 41 |
| Strength to Weight: Axial, points | 20 to 41 | |
| 8.0 |
| Strength to Weight: Bending, points | 36 to 55 | |
| 22 |
| Thermal Diffusivity, mm2/s | 0.1 to 0.51 | |
| 0.12 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 13 |