PET vs. PA 6/10
Both PET and PA 6/10 are thermoplastics. There are 16 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is PET and the bottom bar is PA 6/10.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 3.5 to 11 | |
| 1.6 to 2.3 |
| Elongation at Break, % | 2.5 to 70 | |
| 110 to 120 |
| Flexural Modulus, GPa | 8.3 to 14 | |
| 1.4 to 2.0 |
| Impact Strength: Notched Izod, J/m | 43 to 85 | |
| 85 |
| Tensile Strength: Ultimate (UTS), MPa | 60 to 140 | |
| 45 to 60 |
Thermal Properties
| Maximum Temperature: Decomposition, °C | 390 | |
| 440 |
| Maximum Temperature: Mechanical, °C | 80 | |
| 80 |
| Melting Onset (Solidus), °C | 260 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 1000 to 1150 | |
| 1510 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 3.7 | |
| 3.9 to 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.1 |
| Limiting Oxygen Index (LOI), % | 21 | |
| 25 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.2 to 4.4 | |
| 0.78 to 1.1 |
| Stiffness to Weight: Bending, points | 32 to 54 | |
| 34 to 39 |
| Strength to Weight: Axial, points | 12 to 27 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 25 to 41 | |
| 25 to 30 |