PLA vs. PMMA
Both PLA and PMMA are thermoplastics. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is PLA and the bottom bar is PMMA.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 3.5 | |
| 3.2 |
| Elongation at Break, % | 6.0 | |
| 4.0 |
| Flexural Strength, MPa | 80 | |
| 110 |
| Shear Modulus, GPa | 2.4 | |
| 1.7 |
| Tensile Strength: Ultimate (UTS), MPa | 50 | |
| 71 |
Thermal Properties
| Glass Transition Temperature, °C | 60 | |
| 110 |
| Melting Onset (Solidus), °C | 160 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 1800 | |
| 1260 |
| Thermal Conductivity, W/m-K | 0.13 | |
| 0.19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 | |
| 1.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.6 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 40 | |
| 42 |
| Strength to Weight: Axial, points | 11 | |
| 17 |
| Strength to Weight: Bending, points | 24 | |
| 32 |
| Thermal Diffusivity, mm2/s | 0.058 | |
| 0.13 |