PPE vs. PCTFE
Both PPE and PCTFE are thermoplastics. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is PPE and the bottom bar is PCTFE.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.3 | |
| 1.4 |
| Elongation at Break, % | 30 | |
| 150 |
| Flexural Strength, MPa | 75 | |
| 59 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 36 |
Thermal Properties
| Glass Transition Temperature, °C | 85 | |
| 100 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 120 | |
| 110 |
| Maximum Temperature: Autoignition, °C | 430 | |
| 580 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 150 |
| Melting Onset (Solidus), °C | 260 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 1200 | |
| 920 |
| Thermal Conductivity, W/m-K | 0.22 | |
| 0.21 |
| Thermal Expansion, µm/m-K | 90 | |
| 130 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 19 | |
| 21 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.1 | |
| 2.1 |
| Water Absorption After 24 Hours, % | 0.23 | |
| 0.0094 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.2 | |
| 0.37 |
| Stiffness to Weight: Bending, points | 42 | |
| 17 |
| Strength to Weight: Axial, points | 14 | |
| 4.6 |
| Strength to Weight: Bending, points | 30 | |
| 11 |
| Thermal Diffusivity, mm2/s | 0.17 | |
| 0.11 |
| Thermal Shock Resistance, points | 19 | |
| 14 |