PPO vs. PAR

Both PPO and PAR are thermoplastics. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is PPO and the bottom bar is PAR.

Polyphenylene Oxide (PPO)Polyarylate (PAR)

Metric UnitsUS Customary Units

Mechanical Properties

Elongation at Break, %		3.5 to 28
Elongation at Break, %		50

Flexural Modulus, GPa		2.5 to 8.6
Flexural Modulus, GPa		2.1

Flexural Strength, MPa		92 to 140
Flexural Strength, MPa		75

Impact Strength: Notched Izod, J/m		80 to 270
Impact Strength: Notched Izod, J/m		220

Tensile Strength: Ultimate (UTS), MPa		63 to 140
Tensile Strength: Ultimate (UTS), MPa		67

Thermal Properties

Heat Deflection Temperature At 1.82 MPa (264 psi), °C		120 to 140
Heat Deflection Temperature At 1.82 MPa (264 psi), °C		170

Specific Heat Capacity, J/kg-K		1020 to 1250
Specific Heat Capacity, J/kg-K		1200

Thermal Expansion, µm/m-K		25 to 60
Thermal Expansion, µm/m-K		88

Electrical Properties

Dielectric Constant (Relative Permittivity) At 1 Hz		2.7 to 3.2
Dielectric Constant (Relative Permittivity) At 1 Hz		3.0

Dielectric Strength (Breakdown Potential), kV/mm		19 to 21
Dielectric Strength (Breakdown Potential), kV/mm		16

Electrical Resistivity Order of Magnitude, 10^x Ω-m		15
Electrical Resistivity Order of Magnitude, 10^x Ω-m		12

Otherwise Unclassified Properties

Density, g/cm³		1.1 to 1.4
Density, g/cm³		1.2

Limiting Oxygen Index (LOI), %		32
Limiting Oxygen Index (LOI), %		35

Water Absorption After 24 Hours, %		0.060 to 0.070
Water Absorption After 24 Hours, %		0.26

Common Calculations

Strength to Weight: Axial, points		16 to 27
Strength to Weight: Axial, points		16

Strength to Weight: Bending, points		33 to 42
Strength to Weight: Bending, points		31