PPS vs. PA 6/10
Both PPS and PA 6/10 are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is PPS and the bottom bar is PA 6/10.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.3 to 1.7 | |
| 1.1 |
| Elongation at Break, % | 2.5 to 11 | |
| 110 to 120 |
| Flexural Modulus, GPa | 13 to 17 | |
| 1.4 to 2.0 |
| Flexural Strength, MPa | 120 to 190 | |
| 48 to 59 |
| Impact Strength: Notched Izod, J/m | 21 to 80 | |
| 85 |
| Specific Heat Capacity, J/kg-K | 910 to 1000 | |
| 1510 |
| Strength to Weight: Axial, points | 16 to 37 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 30 to 52 | |
| 25 to 30 |
| Tensile Strength: Ultimate (UTS), MPa | 75 to 190 | |
| 45 to 60 |