PP Copolymer vs. PA 6/6
Both PP copolymer and PA 6/6 are thermoplastics. There are 8 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is PP copolymer and the bottom bar is PA 6/6.
Metric UnitsUS Customary Units
Material Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 2.2 to 2.3 | |
| 3.6 to 15 |
| Dielectric Strength (Breakdown Potential), kV/mm | 21 to 22 | |
| 25 to 30 |
| Elastic (Young's, Tensile) Modulus, GPa | 0.9 to 1.1 | |
| 1.6 to 23 |
| Elongation at Break, % | 12 | |
| 2.8 to 46 |
| Flexural Modulus, GPa | 1.3 | |
| 1.3 to 19 |
| Flexural Strength, MPa | 31 | |
| 80 to 260 |
| Melting Onset (Solidus), °C | 150 | |
| 260 |
| Tensile Strength: Ultimate (UTS), MPa | 23 to 33 | |
| 60 to 240 |