PP Copolymer vs. PPA
Both PP copolymer and PPA are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is PP copolymer and the bottom bar is PPA.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 0.9 to 1.1 | |
| 2.1 to 2.2 |
| Elongation at Break, % | 12 | |
| 30 |
| Flexural Modulus, GPa | 1.3 | |
| 2.3 to 2.4 |
| Flexural Strength, MPa | 31 | |
| 95 to 110 |
| Tensile Strength: Ultimate (UTS), MPa | 23 to 33 | |
| 57 to 69 |
Thermal Properties
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 50 to 100 | |
| 120 |
| Melting Onset (Solidus), °C | 150 | |
| 310 |
Otherwise Unclassified Properties
| Density, g/cm3 | 0.9 | |
| 1.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.56 to 0.68 | |
| 1.0 to 1.1 |
| Stiffness to Weight: Bending, points | 36 to 38 | |
| 38 |
| Strength to Weight: Axial, points | 7.1 to 10 | |
| 14 to 17 |
| Strength to Weight: Bending, points | 20 to 25 | |
| 29 to 33 |