PP Homopolymer vs. MDF
PP homopolymer belongs to the thermoplastics classification, while MDF belongs to the wood-based materials. There are 8 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is PP homopolymer and the bottom bar is MDF.
Metric UnitsUS Customary Units
Material Properties
| Compressive (Crushing) Strength, MPa | 45 to 64 | |
| 10 |
| Density, g/cm3 | 0.91 to 1.2 | |
| 0.75 |
| Elongation at Break, % | 3.0 to 80 | |
| 0.5 |
| Specific Heat Capacity, J/kg-K | 1230 to 1900 | |
| 1700 |
| Strength to Weight: Axial, points | 11 to 21 | |
| 6.7 |
| Strength to Weight: Bending, points | 27 to 37 | |
| 20 |
| Tensile Strength: Ultimate (UTS), MPa | 36 to 93 | |
| 18 |
| Thermal Expansion, µm/m-K | 30 to 90 | |
| 12 |