PVF vs. PA 6/12
Both PVF and PA 6/12 are thermoplastics. There are 11 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is PVF and the bottom bar is PA 6/12.
Metric UnitsUS Customary Units
Mechanical Properties
| Flexural Strength, MPa | 90 | |
| 45 to 64 |
| Tensile Strength: Ultimate (UTS), MPa | 65 | |
| 40 to 58 |
Thermal Properties
| Maximum Temperature: Decomposition, °C | 360 | |
| 450 |
| Melting Onset (Solidus), °C | 230 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 1300 | |
| 1590 |
| Thermal Conductivity, W/m-K | 0.13 | |
| 0.22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.4 | |
| 1.1 |
| Limiting Oxygen Index (LOI), % | 23 | |
| 25 |
Common Calculations
| Strength to Weight: Axial, points | 13 | |
| 10 to 15 |
| Strength to Weight: Bending, points | 26 | |
| 25 to 31 |
| Thermal Diffusivity, mm2/s | 0.071 | |
| 0.13 |