PVDF vs. PP Copolymer
Both PVDF and PP copolymer are thermoplastics. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is PVDF and the bottom bar is PP copolymer.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 1.1 | |
| 0.9 to 1.1 |
| Elongation at Break, % | 200 | |
| 12 |
| Flexural Modulus, GPa | 1.5 | |
| 1.3 |
| Flexural Strength, MPa | 75 | |
| 31 |
| Impact Strength: Notched Izod, J/m | 180 | |
| 110 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 49 | |
| 23 to 33 |
Thermal Properties
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 85 | |
| 50 to 100 |
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 150 | |
| 82 to 98 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 80 |
| Melting Onset (Solidus), °C | 170 | |
| 150 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 Hz | 7.5 | |
| 2.2 to 2.3 |
| Dielectric Strength (Breakdown Potential), kV/mm | 10 | |
| 21 to 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.8 | |
| 0.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.35 | |
| 0.56 to 0.68 |
| Stiffness to Weight: Bending, points | 20 | |
| 36 to 38 |
| Strength to Weight: Axial, points | 7.8 | |
| 7.1 to 10 |
| Strength to Weight: Bending, points | 17 | |
| 20 to 25 |