C-820 Magnesia Ceramic vs. Magnesium Fluoride
C-820 magnesia ceramic belongs to the oxide-based engineering ceramics classification, while magnesium fluoride belongs to the non-glass optical ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C-820 magnesia ceramic and the bottom bar is magnesium fluoride.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.7 | |
| 3.2 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 9.6 | |
| 5.2 |
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 130 |
| Specific Heat Capacity, J/kg-K | 950 | |
| 980 |
| Stiffness to Weight: Axial, points | 21 | |
| 22 |
| Stiffness to Weight: Bending, points | 58 | |
| 52 |
| Thermal Conductivity, W/m-K | 8.0 | |
| 28 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 8.8 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |