QE22A Magnesium vs. SAE-AISI H24 Steel
QE22A magnesium belongs to the magnesium alloys classification, while SAE-AISI H24 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is QE22A magnesium and the bottom bar is SAE-AISI H24 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 44 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 17 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 250 | |
| 720 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 240 |
| Melting Completion (Liquidus), °C | 640 | |
| 1750 |
| Melting Onset (Solidus), °C | 570 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 970 | |
| 420 |
| Thermal Conductivity, W/m-K | 110 | |
| 27 |
| Thermal Expansion, µm/m-K | 27 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.0 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 27 | |
| 6.1 |
| Embodied Energy, MJ/kg | 220 | |
| 93 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 60 | |
| 22 |
| Strength to Weight: Axial, points | 36 | |
| 22 to 61 |
| Strength to Weight: Bending, points | 46 | |
| 20 to 39 |
| Thermal Diffusivity, mm2/s | 59 | |
| 6.9 |
| Thermal Shock Resistance, points | 15 | |
| 22 to 61 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0.42 to 0.53 |
| Chromium (Cr), % | 0 | |
| 2.5 to 3.5 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 | |
| 78 to 82.4 |
| Magnesium (Mg), % | 93.1 to 95.8 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.15 to 0.4 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.4 |
| Silver (Ag), % | 2.0 to 3.0 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 14 to 16 |
| Unspecified Rare Earths, % | 1.8 to 2.5 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.4 to 0.6 |
| Zirconium (Zr), % | 0.4 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |