Quarter-hard AISI 304L vs. Quarter-hard 85-silver 15-cadmium-oxide
Quarter-hard AISI 304L belongs to the iron alloys classification, while quarter-hard 85-silver 15-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is quarter-hard AISI 304L and the bottom bar is quarter-hard 85-silver 15-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.8 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 73 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 65 |
| Elongation at Break, % | 11 | |
| 2.2 |
| Shear Strength, MPa | 590 | |
| 210 |
| Strength to Weight: Axial, points | 35 | |
| 10 |
| Strength to Weight: Bending, points | 28 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 980 | |
| 370 |