Quarter-hard 60Pd-40Ag Alloy vs. Quarter-hard Silver
Both quarter-hard 60Pd-40Ag alloy and quarter-hard silver are otherwise unclassified metals. Both are furnished in the quarter-hard temper. They have a modest 40% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is quarter-hard 60Pd-40Ag alloy and the bottom bar is quarter-hard silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 71 |
| Elongation at Break, % | 1.1 | |
| 4.6 |
| Poisson's Ratio | 0.38 | |
| 0.37 |
| Shear Modulus, GPa | 37 | |
| 26 |
| Shear Strength, MPa | 290 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 520 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 110 |
| Melting Completion (Liquidus), °C | 1360 | |
| 960 |
| Melting Onset (Solidus), °C | 1310 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 240 |
| Thermal Conductivity, W/m-K | 29 | |
| 420 |
| Thermal Expansion, µm/m-K | 15 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 4.1 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 87 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.9 | |
| 3.8 |
| Stiffness to Weight: Bending, points | 14 | |
| 13 |
| Strength to Weight: Axial, points | 13 | |
| 6.1 |
| Strength to Weight: Bending, points | 13 | |
| 8.0 |
| Thermal Diffusivity, mm2/s | 11 | |
| 170 |
| Thermal Shock Resistance, points | 25 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Palladium (Pd), % | 59.5 to 60.9 | |
| 0 |
| Silver (Ag), % | 39.1 to 40.5 | |
| 99.9 to 100 |
| Residuals, % | 0 to 0.3 | |
| 0 to 0.1 |