Reactor Grade Zirconium vs. Grade 366 Molybdenum
Both reactor grade zirconium and grade 366 molybdenum are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is reactor grade zirconium and the bottom bar is grade 366 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 300 |
| Elongation at Break, % | 21 | |
| 2.2 |
| Poisson's Ratio | 0.34 | |
| 0.3 |
| Shear Modulus, GPa | 37 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 330 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 210 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 7.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.5 | |
| 12 |
| Embodied Water, L/kg | 280 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 370 |
| Stiffness to Weight: Axial, points | 8.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 14 | |
| 13 |
| Strength to Weight: Bending, points | 16 | |
| 13 |
| Thermal Shock Resistance, points | 41 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Iron (Fe), % | 0 | |
| 0 to 0.010 |
| Molybdenum (Mo), % | 0 | |
| 66.9 to 73 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Nitrogen (N), % | 0 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 | |
| 0 to 0.0025 |
| Silicon (Si), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 27 to 33 |
| Zirconium (Zr), % | 99.7 to 100 | |
| 0 |
| Residuals, % | 0 to 0.27 | |
| 0 |