Reactor Grade Zirconium vs. C14500 Copper
Reactor grade zirconium belongs to the otherwise unclassified metals classification, while C14500 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is reactor grade zirconium and the bottom bar is C14500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 120 |
| Elongation at Break, % | 21 | |
| 12 to 50 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 37 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 330 | |
| 220 to 330 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 69 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 390 |
| Thermal Conductivity, W/m-K | 22 | |
| 360 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.5 | |
| 8.9 |
| Embodied Water, L/kg | 280 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 36 to 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 21 to 300 |
| Stiffness to Weight: Axial, points | 8.4 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 14 | |
| 6.8 to 10 |
| Strength to Weight: Bending, points | 16 | |
| 9.1 to 12 |
| Thermal Diffusivity, mm2/s | 13 | |
| 100 |
| Thermal Shock Resistance, points | 41 | |
| 8.0 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 | |
| 99.2 to 99.596 |
| Phosphorus (P), % | 0 | |
| 0.0040 to 0.012 |
| Tellurium (Te), % | 0 | |
| 0.4 to 0.7 |
| Zirconium (Zr), % | 99.7 to 100 | |
| 0 |
| Residuals, % | 0 to 0.27 | |
| 0 |