Reactor Grade Zirconium vs. S30615 Stainless Steel
Reactor grade zirconium belongs to the otherwise unclassified metals classification, while S30615 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is reactor grade zirconium and the bottom bar is S30615 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 190 |
| Elongation at Break, % | 21 | |
| 39 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 37 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 330 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 340 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 500 |
| Thermal Conductivity, W/m-K | 22 | |
| 14 |
| Thermal Expansion, µm/m-K | 5.9 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.5 | |
| 7.6 |
| Embodied Water, L/kg | 280 | |
| 170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 | |
| 260 |
| Stiffness to Weight: Axial, points | 8.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 14 | |
| 25 |
| Strength to Weight: Bending, points | 16 | |
| 23 |
| Thermal Diffusivity, mm2/s | 13 | |
| 3.7 |
| Thermal Shock Resistance, points | 41 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.8 to 1.5 |
| Carbon (C), % | 0 | |
| 0.16 to 0.24 |
| Chromium (Cr), % | 0 | |
| 17 to 19.5 |
| Iron (Fe), % | 0 | |
| 56.7 to 65.3 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 13.5 to 16 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 3.2 to 4.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zirconium (Zr), % | 99.7 to 100 | |
| 0 |
| Residuals, % | 0 to 0.27 | |
| 0 |