RPU vs. UPVC
RPU belongs to the thermoset plastics classification, while uPVC belongs to the thermoplastics. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is RPU and the bottom bar is uPVC.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 2.2 | |
| 3.7 |
| Elongation at Break, % | 90 | |
| 58 |
| Flexural Modulus, GPa | 2.0 | |
| 3.5 |
| Flexural Strength, MPa | 83 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 60 | |
| 47 |
Thermal Properties
| Maximum Temperature: Autoignition, °C | 380 | |
| 400 |
| Maximum Temperature: Decomposition, °C | 270 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 1750 | |
| 880 |
| Thermal Conductivity, W/m-K | 0.19 | |
| 0.16 |
| Thermal Expansion, µm/m-K | 63 | |
| 61 |
| Vicat Softening Temperature, °C | 120 | |
| 83 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 19 | |
| 19 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.2 | |
| 1.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.0 | |
| 1.5 |
| Stiffness to Weight: Bending, points | 36 | |
| 37 |
| Strength to Weight: Axial, points | 14 | |
| 9.1 |
| Strength to Weight: Bending, points | 28 | |
| 20 |
| Thermal Diffusivity, mm2/s | 0.090 | |
| 0.13 |
| Thermal Shock Resistance, points | 31 | |
| 15 |