Z13004 Zinc vs. AISI 317LM Stainless Steel

Z13004 zinc belongs to the zinc alloys classification, while AISI 317LM stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is AISI 317LM stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 30
46
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
79
Tensile Strength: Ultimate (UTS), MPa 93
590
Tensile Strength: Yield (Proof), MPa 76
230

Thermal Properties

Latent Heat of Fusion, J/g 110
300
Maximum Temperature: Mechanical, °C 90
300
Melting Completion (Liquidus), °C 410
1460
Melting Onset (Solidus), °C 390
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
14
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 37
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 11
24
Density, g/cm3 6.6
8.0
Embodied Carbon, kg CO2/kg material 2.8
4.8
Embodied Energy, MJ/kg 53
65
Embodied Water, L/kg 340
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
210
Resilience: Unit (Modulus of Resilience), kJ/m3 33
130
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 3.9
21
Strength to Weight: Bending, points 7.0
20
Thermal Diffusivity, mm2/s 44
3.8
Thermal Shock Resistance, points 2.9
13

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
18 to 20
Copper (Cu), % 0 to 0.0030
0
Iron (Fe), % 0 to 0.0030
54.4 to 64.5
Lead (Pb), % 0 to 0.0030
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 0
13.5 to 17.5
Nitrogen (N), % 0
0 to 0.2
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0010
0
Zinc (Zn), % 99.985 to 100
0