Z13004 Zinc vs. ASTM B617 Coin Silver

Z13004 zinc belongs to the zinc alloys classification, while ASTM B617 coin silver belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is ASTM B617 coin silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
75
Elongation at Break, % 30
1.1 to 22
Poisson's Ratio 0.25
0.37
Shear Modulus, GPa 35
28
Tensile Strength: Ultimate (UTS), MPa 93
290 to 520

Thermal Properties

Latent Heat of Fusion, J/g 110
120
Melting Completion (Liquidus), °C 410
870
Melting Onset (Solidus), °C 390
780
Specific Heat Capacity, J/kg-K 390
250
Thermal Expansion, µm/m-K 26
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
83
Electrical Conductivity: Equal Weight (Specific), % IACS 37
72

Otherwise Unclassified Properties

Density, g/cm3 6.6
10

Common Calculations

Stiffness to Weight: Axial, points 7.4
4.1
Stiffness to Weight: Bending, points 23
14
Strength to Weight: Axial, points 3.9
7.7 to 14
Strength to Weight: Bending, points 7.0
9.3 to 14
Thermal Shock Resistance, points 2.9
14 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0020
0 to 0.0050
Cadmium (Cd), % 0 to 0.0030
0 to 0.050
Copper (Cu), % 0 to 0.0030
9.0 to 10.4
Iron (Fe), % 0 to 0.0030
0 to 0.050
Lead (Pb), % 0 to 0.0030
0 to 0.030
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.020
Silver (Ag), % 0
89.6 to 91
Tin (Sn), % 0 to 0.0010
0
Zinc (Zn), % 99.985 to 100
0 to 0.060
Residuals, % 0
0 to 0.060