Z13004 Zinc vs. ASTM B631 Class C

Z13004 zinc belongs to the zinc alloys classification, while ASTM B631 class C belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is ASTM B631 class C.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
180 to 190
Poisson's Ratio 0.25
0.32
Shear Modulus, GPa 35
66 to 71

Thermal Properties

Latent Heat of Fusion, J/g 110
140 to 150
Melting Completion (Liquidus), °C 410
2090 to 2230
Specific Heat Capacity, J/kg-K 390
180
Thermal Conductivity, W/m-K 110
450 to 490
Thermal Expansion, µm/m-K 26
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
55 to 63
Electrical Conductivity: Equal Weight (Specific), % IACS 37
36 to 43

Otherwise Unclassified Properties

Density, g/cm3 6.6
13 to 14
Embodied Carbon, kg CO2/kg material 2.8
55 to 59
Embodied Energy, MJ/kg 53
860 to 920

Common Calculations

Stiffness to Weight: Axial, points 7.4
7.4 to 7.6
Stiffness to Weight: Bending, points 23
14
Thermal Diffusivity, mm2/s 44
180 to 200