Z13004 Zinc vs. AWS BAg-9

Z13004 zinc belongs to the zinc alloys classification, while AWS BAg-9 belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is AWS BAg-9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
82
Poisson's Ratio 0.25
0.35
Shear Modulus, GPa 35
31
Tensile Strength: Ultimate (UTS), MPa 93
140

Thermal Properties

Latent Heat of Fusion, J/g 110
130
Melting Completion (Liquidus), °C 410
720
Melting Onset (Solidus), °C 390
670
Specific Heat Capacity, J/kg-K 390
290
Thermal Expansion, µm/m-K 26
20

Otherwise Unclassified Properties

Density, g/cm3 6.6
9.6
Embodied Energy, MJ/kg 53
980

Common Calculations

Stiffness to Weight: Axial, points 7.4
4.8
Stiffness to Weight: Bending, points 23
15
Strength to Weight: Axial, points 3.9
4.1
Strength to Weight: Bending, points 7.0
6.3
Thermal Shock Resistance, points 2.9
6.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Copper (Cu), % 0 to 0.0030
19 to 21
Iron (Fe), % 0 to 0.0030
0
Lead (Pb), % 0 to 0.0030
0
Silver (Ag), % 0
64 to 66
Tin (Sn), % 0 to 0.0010
0
Zinc (Zn), % 99.985 to 100
13 to 17
Residuals, % 0
0 to 0.15