Z13004 Zinc vs. EN 1.4587 Stainless Steel

Z13004 zinc belongs to the zinc alloys classification, while EN 1.4587 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is EN 1.4587 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 30
34
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
80
Tensile Strength: Ultimate (UTS), MPa 93
540
Tensile Strength: Yield (Proof), MPa 76
250

Thermal Properties

Latent Heat of Fusion, J/g 110
310
Maximum Temperature: Mechanical, °C 90
1100
Melting Completion (Liquidus), °C 410
1420
Melting Onset (Solidus), °C 390
1370
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
17
Thermal Expansion, µm/m-K 26
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 37
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 11
36
Density, g/cm3 6.6
8.1
Embodied Carbon, kg CO2/kg material 2.8
6.3
Embodied Energy, MJ/kg 53
87
Embodied Water, L/kg 340
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
150
Resilience: Unit (Modulus of Resilience), kJ/m3 33
150
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 3.9
18
Strength to Weight: Bending, points 7.0
18
Thermal Diffusivity, mm2/s 44
4.5
Thermal Shock Resistance, points 2.9
13

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 0 to 0.0030
2.0 to 3.0
Iron (Fe), % 0 to 0.0030
32.7 to 41.9
Lead (Pb), % 0 to 0.0030
0
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
4.0 to 5.0
Nickel (Ni), % 0
28 to 30
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.025
Tin (Sn), % 0 to 0.0010
0
Zinc (Zn), % 99.985 to 100
0