Z13004 Zinc vs. EN 1.4835 Stainless Steel

Z13004 zinc belongs to the zinc alloys classification, while EN 1.4835 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is EN 1.4835 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 30
43
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
77
Tensile Strength: Ultimate (UTS), MPa 93
750
Tensile Strength: Yield (Proof), MPa 76
350

Thermal Properties

Latent Heat of Fusion, J/g 110
320
Maximum Temperature: Mechanical, °C 90
1150
Melting Completion (Liquidus), °C 410
1400
Melting Onset (Solidus), °C 390
1360
Specific Heat Capacity, J/kg-K 390
490
Thermal Conductivity, W/m-K 110
15
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 37
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 11
17
Density, g/cm3 6.6
7.7
Embodied Carbon, kg CO2/kg material 2.8
3.3
Embodied Energy, MJ/kg 53
47
Embodied Water, L/kg 340
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
270
Resilience: Unit (Modulus of Resilience), kJ/m3 33
310
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 3.9
27
Strength to Weight: Bending, points 7.0
24
Thermal Diffusivity, mm2/s 44
4.0
Thermal Shock Resistance, points 2.9
16

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 0
20 to 22
Copper (Cu), % 0 to 0.0030
0
Iron (Fe), % 0 to 0.0030
62 to 68.4
Lead (Pb), % 0 to 0.0030
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
10 to 12
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0
1.4 to 2.5
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.0010
0
Zinc (Zn), % 99.985 to 100
0