Z13004 Zinc vs. Grade 704C Zirconium

Z13004 zinc belongs to the zinc alloys classification, while grade 704C zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is grade 704C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
97
Elongation at Break, % 30
11
Poisson's Ratio 0.25
0.34
Shear Modulus, GPa 35
36
Tensile Strength: Ultimate (UTS), MPa 93
470
Tensile Strength: Yield (Proof), MPa 76
310

Thermal Properties

Latent Heat of Fusion, J/g 110
240
Specific Heat Capacity, J/kg-K 390
270
Thermal Conductivity, W/m-K 110
21
Thermal Expansion, µm/m-K 26
5.9

Otherwise Unclassified Properties

Density, g/cm3 6.6
6.7
Embodied Water, L/kg 340
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
48
Resilience: Unit (Modulus of Resilience), kJ/m3 33
490
Stiffness to Weight: Axial, points 7.4
8.1
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 3.9
20
Strength to Weight: Bending, points 7.0
20
Thermal Diffusivity, mm2/s 44
12
Thermal Shock Resistance, points 2.9
58

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 0 to 0.0030
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 0.0030
0 to 0.3
Lead (Pb), % 0 to 0.0030
0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.010
Tin (Sn), % 0 to 0.0010
1.0 to 2.0
Zinc (Zn), % 99.985 to 100
0
Zirconium (Zr), % 0
92.9 to 99