MakeItFrom.com
Menu (ESC)

Z13004 Zinc vs. Grade N12MV Nickel

Z13004 zinc belongs to the zinc alloys classification, while grade N12MV nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is grade N12MV nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
220
Elongation at Break, % 30
6.8
Poisson's Ratio 0.25
0.31
Shear Modulus, GPa 35
84
Tensile Strength: Ultimate (UTS), MPa 93
600
Tensile Strength: Yield (Proof), MPa 76
310

Thermal Properties

Latent Heat of Fusion, J/g 110
320
Maximum Temperature: Mechanical, °C 90
900
Melting Completion (Liquidus), °C 410
1620
Melting Onset (Solidus), °C 390
1570
Specific Heat Capacity, J/kg-K 390
390
Thermal Expansion, µm/m-K 26
10

Otherwise Unclassified Properties

Base Metal Price, % relative 11
75
Density, g/cm3 6.6
9.2
Embodied Carbon, kg CO2/kg material 2.8
16
Embodied Energy, MJ/kg 53
200
Embodied Water, L/kg 340
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
34
Resilience: Unit (Modulus of Resilience), kJ/m3 33
220
Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
22
Strength to Weight: Axial, points 3.9
18
Strength to Weight: Bending, points 7.0
17
Thermal Shock Resistance, points 2.9
19

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0
0 to 1.0
Copper (Cu), % 0 to 0.0030
0
Iron (Fe), % 0 to 0.0030
4.0 to 6.0
Lead (Pb), % 0 to 0.0030
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
26 to 30
Nickel (Ni), % 0
60.2 to 69.8
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.0010
0
Vanadium (V), % 0
0.2 to 0.6
Zinc (Zn), % 99.985 to 100
0