Z13004 Zinc vs. Grade Ti-Pd7B Titanium

Z13004 zinc belongs to the zinc alloys classification, while grade Ti-Pd7B titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is grade Ti-Pd7B titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
110
Elongation at Break, % 30
17
Poisson's Ratio 0.25
0.32
Shear Modulus, GPa 35
40
Tensile Strength: Ultimate (UTS), MPa 93
390
Tensile Strength: Yield (Proof), MPa 76
310

Thermal Properties

Latent Heat of Fusion, J/g 110
420
Maximum Temperature: Mechanical, °C 90
320
Melting Completion (Liquidus), °C 410
1660
Melting Onset (Solidus), °C 390
1610
Specific Heat Capacity, J/kg-K 390
540
Thermal Conductivity, W/m-K 110
22
Thermal Expansion, µm/m-K 26
8.7

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
3.6
Electrical Conductivity: Equal Weight (Specific), % IACS 37
7.1

Otherwise Unclassified Properties

Density, g/cm3 6.6
4.5
Embodied Carbon, kg CO2/kg material 2.8
49
Embodied Energy, MJ/kg 53
840
Embodied Water, L/kg 340
520

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
62
Resilience: Unit (Modulus of Resilience), kJ/m3 33
440
Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
35
Strength to Weight: Axial, points 3.9
24
Strength to Weight: Bending, points 7.0
26
Thermal Diffusivity, mm2/s 44
8.9
Thermal Shock Resistance, points 2.9
30

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 0 to 0.0030
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0 to 0.0030
0 to 0.2
Lead (Pb), % 0 to 0.0030
0
Nickel (Ni), % 0
0 to 0.050
Oxygen (O), % 0
0 to 0.4
Palladium (Pd), % 0
0.12 to 0.3
Tin (Sn), % 0 to 0.0010
0
Titanium (Ti), % 0
98.8 to 99.9
Zinc (Zn), % 99.985 to 100
0
Residuals, % 0
0 to 0.4