Z13004 Zinc vs. C67300 Bronze

Z13004 zinc belongs to the zinc alloys classification, while C67300 bronze belongs to the copper alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is C67300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
110
Elongation at Break, % 30
12
Poisson's Ratio 0.25
0.31
Shear Modulus, GPa 35
41
Tensile Strength: Ultimate (UTS), MPa 93
500
Tensile Strength: Yield (Proof), MPa 76
340

Thermal Properties

Latent Heat of Fusion, J/g 110
190
Maximum Temperature: Mechanical, °C 90
130
Melting Completion (Liquidus), °C 410
870
Melting Onset (Solidus), °C 390
830
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 110
95
Thermal Expansion, µm/m-K 26
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
22
Electrical Conductivity: Equal Weight (Specific), % IACS 37
25

Otherwise Unclassified Properties

Base Metal Price, % relative 11
23
Density, g/cm3 6.6
8.0
Embodied Carbon, kg CO2/kg material 2.8
2.7
Embodied Energy, MJ/kg 53
46
Embodied Water, L/kg 340
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
55
Resilience: Unit (Modulus of Resilience), kJ/m3 33
550
Stiffness to Weight: Axial, points 7.4
7.4
Stiffness to Weight: Bending, points 23
20
Strength to Weight: Axial, points 3.9
17
Strength to Weight: Bending, points 7.0
17
Thermal Diffusivity, mm2/s 44
30
Thermal Shock Resistance, points 2.9
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.0020
0 to 0.25
Cadmium (Cd), % 0 to 0.0030
0
Copper (Cu), % 0 to 0.0030
58 to 63
Iron (Fe), % 0 to 0.0030
0 to 0.5
Lead (Pb), % 0 to 0.0030
0.4 to 3.0
Manganese (Mn), % 0
2.0 to 3.5
Nickel (Ni), % 0
0 to 0.25
Silicon (Si), % 0
0.5 to 1.5
Tin (Sn), % 0 to 0.0010
0 to 0.3
Zinc (Zn), % 99.985 to 100
27.2 to 39.1
Residuals, % 0
0 to 0.5