Z13004 Zinc vs. C89320 Bronze
Z13004 zinc belongs to the zinc alloys classification, while C89320 bronze belongs to the copper alloys.
For each property being compared, the top bar is Z13004 zinc and the bottom bar is C89320 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 110 |
| Elongation at Break, % | 30 | |
| 17 |
| Poisson's Ratio | 0.25 | |
| 0.34 |
| Shear Modulus, GPa | 35 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 93 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 76 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 90 | |
| 180 |
| Melting Completion (Liquidus), °C | 410 | |
| 1050 |
| Melting Onset (Solidus), °C | 390 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 360 |
| Thermal Conductivity, W/m-K | 110 | |
| 56 |
| Thermal Expansion, µm/m-K | 26 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 27 | |
| 15 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 37 |
| Density, g/cm3 | 6.6 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.5 |
| Embodied Energy, MJ/kg | 53 | |
| 56 |
| Embodied Water, L/kg | 340 | |
| 490 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 | |
| 38 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 33 | |
| 93 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 3.9 | |
| 8.5 |
| Strength to Weight: Bending, points | 7.0 | |
| 10 |
| Thermal Diffusivity, mm2/s | 44 | |
| 17 |
| Thermal Shock Resistance, points | 2.9 | |
| 10 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0020 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.35 |
| Bismuth (Bi), % | 0 | |
| 4.0 to 6.0 |
| Cadmium (Cd), % | 0 to 0.0030 | |
| 0 |
| Copper (Cu), % | 0 to 0.0030 | |
| 87 to 91 |
| Iron (Fe), % | 0 to 0.0030 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.0030 | |
| 0 to 0.090 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 to 0.0010 | |
| 5.0 to 7.0 |
| Zinc (Zn), % | 99.985 to 100 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |