Z13004 Zinc vs. R60802 Alloy
Z13004 zinc belongs to the zinc alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is Z13004 zinc and the bottom bar is R60802 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 87 | |
| 98 |
| Elongation at Break, % | 30 | |
| 22 |
| Poisson's Ratio | 0.25 | |
| 0.34 |
| Shear Modulus, GPa | 35 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 93 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 76 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 270 |
| Thermal Conductivity, W/m-K | 110 | |
| 22 |
| Thermal Expansion, µm/m-K | 26 | |
| 6.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 6.6 | |
| 6.5 |
| Embodied Water, L/kg | 340 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 26 | |
| 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 33 | |
| 380 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 3.9 | |
| 18 |
| Strength to Weight: Bending, points | 7.0 | |
| 19 |
| Thermal Diffusivity, mm2/s | 44 | |
| 12 |
| Thermal Shock Resistance, points | 2.9 | |
| 53 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.0020 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0030 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.050 to 0.15 |
| Copper (Cu), % | 0 to 0.0030 | |
| 0 |
| Iron (Fe), % | 0 to 0.0030 | |
| 0.070 to 0.2 |
| Lead (Pb), % | 0 to 0.0030 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.030 to 0.080 |
| Tin (Sn), % | 0 to 0.0010 | |
| 1.2 to 1.7 |
| Zinc (Zn), % | 99.985 to 100 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 97.8 to 98.7 |
| Residuals, % | 0 | |
| 0 to 0.11 |