Z13004 Zinc vs. S31277 Stainless Steel

Z13004 zinc belongs to the zinc alloys classification, while S31277 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is Z13004 zinc and the bottom bar is S31277 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
210
Elongation at Break, % 30
45
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 35
80
Tensile Strength: Ultimate (UTS), MPa 93
860
Tensile Strength: Yield (Proof), MPa 76
410

Thermal Properties

Latent Heat of Fusion, J/g 110
310
Maximum Temperature: Mechanical, °C 90
1100
Melting Completion (Liquidus), °C 410
1460
Melting Onset (Solidus), °C 390
1410
Specific Heat Capacity, J/kg-K 390
460
Thermal Expansion, µm/m-K 26
16

Otherwise Unclassified Properties

Base Metal Price, % relative 11
36
Density, g/cm3 6.6
8.1
Embodied Carbon, kg CO2/kg material 2.8
6.7
Embodied Energy, MJ/kg 53
90
Embodied Water, L/kg 340
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 26
320
Resilience: Unit (Modulus of Resilience), kJ/m3 33
410
Stiffness to Weight: Axial, points 7.4
14
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 3.9
29
Strength to Weight: Bending, points 7.0
25
Thermal Shock Resistance, points 2.9
19

Alloy Composition

Aluminum (Al), % 0 to 0.0020
0
Cadmium (Cd), % 0 to 0.0030
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
20.5 to 23
Copper (Cu), % 0 to 0.0030
0.5 to 1.5
Iron (Fe), % 0 to 0.0030
35.5 to 46.2
Lead (Pb), % 0 to 0.0030
0
Manganese (Mn), % 0
0 to 3.0
Molybdenum (Mo), % 0
6.5 to 8.0
Nickel (Ni), % 0
26 to 28
Nitrogen (N), % 0
0.3 to 0.4
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 0 to 0.0010
0
Zinc (Zn), % 99.985 to 100
0