SAE-AISI 1008 Steel vs. R30035 Cobalt

SAE-AISI 1008 steel belongs to the iron alloys classification, while R30035 cobalt belongs to the cobalt alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1008 steel and the bottom bar is R30035 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220 to 230
Elongation at Break, % 22 to 33
9.0 to 46
Fatigue Strength, MPa 150 to 220
170 to 740
Poisson's Ratio 0.29
0.29
Reduction in Area, % 50 to 63
40 to 74
Shear Modulus, GPa 73
84 to 89
Tensile Strength: Ultimate (UTS), MPa 330 to 370
900 to 1900
Tensile Strength: Yield (Proof), MPa 190 to 310
300 to 1650

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1320
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 62
11
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
100
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 1.4
10
Embodied Energy, MJ/kg 18
140
Embodied Water, L/kg 45
410

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78 to 91
160 to 320
Resilience: Unit (Modulus of Resilience), kJ/m3 92 to 260
210 to 5920
Stiffness to Weight: Axial, points 13
14 to 15
Stiffness to Weight: Bending, points 24
23 to 24
Strength to Weight: Axial, points 12 to 13
29 to 61
Strength to Weight: Bending, points 13 to 15
24 to 39
Thermal Diffusivity, mm2/s 17
3.0
Thermal Shock Resistance, points 10 to 12
23 to 46

Alloy Composition

Boron (B), % 0
0 to 0.015
Carbon (C), % 0 to 0.1
0 to 0.025
Chromium (Cr), % 0
19 to 21
Cobalt (Co), % 0
29.1 to 39
Iron (Fe), % 99.31 to 99.7
0 to 1.0
Manganese (Mn), % 0.3 to 0.5
0 to 0.15
Molybdenum (Mo), % 0
9.0 to 10.5
Nickel (Ni), % 0
33 to 37
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0
0 to 0.15
Sulfur (S), % 0 to 0.050
0 to 0.010
Titanium (Ti), % 0
0 to 1.0

Comparable Variants