SAE-AISI 1010 Steel vs. R31538 Cobalt

SAE-AISI 1010 steel belongs to the iron alloys classification, while R31538 cobalt belongs to the cobalt alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1010 steel and the bottom bar is R31538 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 22 to 31
13 to 23
Fatigue Strength, MPa 150 to 230
310 to 480
Poisson's Ratio 0.29
0.29
Reduction in Area, % 46 to 56
13 to 22
Shear Modulus, GPa 73
86
Tensile Strength: Ultimate (UTS), MPa 350 to 400
1020 to 1360
Tensile Strength: Yield (Proof), MPa 190 to 330
580 to 930

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Melting Completion (Liquidus), °C 1470
1360
Melting Onset (Solidus), °C 1430
1290
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 47
13
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 14
2.1

Otherwise Unclassified Properties

Density, g/cm3 7.9
8.4
Embodied Carbon, kg CO2/kg material 1.4
8.1
Embodied Energy, MJ/kg 18
110
Embodied Water, L/kg 45
530

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82 to 93
140 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 100 to 290
750 to 1920
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 12 to 14
34 to 45
Strength to Weight: Bending, points 14 to 15
27 to 32
Thermal Diffusivity, mm2/s 13
3.5
Thermal Shock Resistance, points 11 to 13
25 to 33

Alloy Composition

Carbon (C), % 0.080 to 0.13
0.15 to 0.35
Chromium (Cr), % 0
26 to 30
Cobalt (Co), % 0
58.7 to 68.9
Iron (Fe), % 99.18 to 99.62
0 to 0.75
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 7.0
Nickel (Ni), % 0
0 to 1.0
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.050
0

Comparable Variants