SAE-AISI 1018 Steel vs. Grade CU5MCuC Nickel

SAE-AISI 1018 steel belongs to the iron alloys classification, while grade CU5MCuC nickel belongs to the nickel alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1018 steel and the bottom bar is grade CU5MCuC nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17 to 27
22
Fatigue Strength, MPa 180 to 270
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 430 to 480
580
Tensile Strength: Yield (Proof), MPa 240 to 400
270

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
45
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 1.4
7.7
Embodied Energy, MJ/kg 18
110
Embodied Water, L/kg 46
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75 to 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 150 to 430
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15 to 17
20
Strength to Weight: Bending, points 16 to 17
19
Thermal Shock Resistance, points 14 to 15
16

Alloy Composition

Carbon (C), % 0.15 to 0.2
0 to 0.050
Chromium (Cr), % 0
19.5 to 23.5
Copper (Cu), % 0
1.5 to 3.5
Iron (Fe), % 98.8 to 99.25
22.2 to 37.9
Manganese (Mn), % 0.6 to 0.9
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0
38 to 44
Niobium (Nb), % 0
0.6 to 1.2
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030