SAE-AISI 1030 Steel vs. CC212E Bronze

SAE-AISI 1030 steel belongs to the iron alloys classification, while CC212E bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1030 steel and the bottom bar is CC212E bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 160
170
Elastic (Young's, Tensile) Modulus, GPa 190
130
Elongation at Break, % 14 to 22
20
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
47
Tensile Strength: Ultimate (UTS), MPa 530 to 590
710
Tensile Strength: Yield (Proof), MPa 300 to 490
310

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Maximum Temperature: Mechanical, °C 400
220
Melting Completion (Liquidus), °C 1460
1080
Melting Onset (Solidus), °C 1420
1020
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 12
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
27
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.4
3.4
Embodied Energy, MJ/kg 18
55
Embodied Water, L/kg 46
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 77 to 100
120
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 650
390
Stiffness to Weight: Axial, points 13
8.5
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 19 to 21
24
Strength to Weight: Bending, points 18 to 20
21
Thermal Shock Resistance, points 17 to 19
22

Alloy Composition

Aluminum (Al), % 0
7.0 to 9.0
Carbon (C), % 0.28 to 0.34
0
Copper (Cu), % 0
68 to 77
Iron (Fe), % 98.7 to 99.12
2.0 to 4.0
Lead (Pb), % 0
0 to 0.050
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0.6 to 0.9
8.0 to 15
Nickel (Ni), % 0
1.5 to 4.5
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0
0 to 0.1
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0
0 to 0.5
Zinc (Zn), % 0
0 to 1.0