SAE-AISI 1030 Steel vs. S28200 Stainless Steel

Both SAE-AISI 1030 steel and S28200 stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1030 steel and the bottom bar is S28200 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 160
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14 to 22
45
Fatigue Strength, MPa 210 to 320
430
Poisson's Ratio 0.29
0.28
Reduction in Area, % 39 to 48
57
Shear Modulus, GPa 73
77
Shear Strength, MPa 330 to 360
610
Tensile Strength: Ultimate (UTS), MPa 530 to 590
870
Tensile Strength: Yield (Proof), MPa 300 to 490
460

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
900
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1330
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
12
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 18
41
Embodied Water, L/kg 46
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 77 to 100
330
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 650
540
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 19 to 21
32
Strength to Weight: Bending, points 18 to 20
27
Thermal Shock Resistance, points 17 to 19
17

Alloy Composition

Carbon (C), % 0.28 to 0.34
0 to 0.15
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 0
0.75 to 1.3
Iron (Fe), % 98.7 to 99.12
57.7 to 64.1
Manganese (Mn), % 0.6 to 0.9
17 to 19
Molybdenum (Mo), % 0
0.75 to 1.3
Nitrogen (N), % 0
0.4 to 0.6
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.030