SAE-AISI 1037 Steel vs. S45503 Stainless Steel
Both SAE-AISI 1037 steel and S45503 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1037 steel and the bottom bar is S45503 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 190 | |
| 410 to 500 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 20 | |
| 4.6 to 6.8 |
| Fatigue Strength, MPa | 220 to 340 | |
| 710 to 800 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Reduction in Area, % | 40 to 45 | |
| 17 to 28 |
| Shear Modulus, GPa | 73 | |
| 75 |
| Shear Strength, MPa | 360 to 390 | |
| 940 to 1070 |
| Tensile Strength: Ultimate (UTS), MPa | 580 to 640 | |
| 1610 to 1850 |
| Tensile Strength: Yield (Proof), MPa | 320 to 540 | |
| 1430 to 1700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 760 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1440 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 15 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.4 |
| Embodied Energy, MJ/kg | 18 | |
| 48 |
| Embodied Water, L/kg | 46 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 100 | |
| 82 to 110 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 23 | |
| 57 to 65 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 39 to 43 |
| Thermal Shock Resistance, points | 18 to 20 | |
| 56 to 64 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.38 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Copper (Cu), % | 0 | |
| 1.5 to 2.5 |
| Iron (Fe), % | 98.5 to 99 | |
| 72.4 to 78.9 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 7.5 to 9.5 |
| Niobium (Nb), % | 0 | |
| 0.1 to 0.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 1.0 to 1.4 |