SAE-AISI 1038 Steel vs. ASTM A225 Steel

Both SAE-AISI 1038 steel and ASTM A225 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1038 steel and the bottom bar is ASTM A225 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 180
190 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14 to 20
21 to 23
Fatigue Strength, MPa 220 to 350
330 to 390
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 370 to 390
390 to 520
Tensile Strength: Ultimate (UTS), MPa 590 to 640
620 to 830
Tensile Strength: Yield (Proof), MPa 320 to 540
460 to 550

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
52
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 18
24 to 25
Embodied Water, L/kg 46
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 100
120 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 270 to 790
580 to 820
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 23
22 to 29
Strength to Weight: Bending, points 20 to 21
21 to 25
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 19 to 20
18 to 24

Comparable Variants