SAE-AISI 1042 Steel vs. EN 1.0213 Steel
Both SAE-AISI 1042 steel and EN 1.0213 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is SAE-AISI 1042 steel and the bottom bar is EN 1.0213 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 200 | |
| 92 to 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 18 | |
| 12 to 25 |
| Fatigue Strength, MPa | 230 to 370 | |
| 160 to 240 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 39 to 50 | |
| 72 to 80 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 380 to 420 | |
| 230 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 700 | |
| 320 to 430 |
| Tensile Strength: Yield (Proof), MPa | 340 to 580 | |
| 220 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1470 |
| Melting Onset (Solidus), °C | 1420 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 | |
| 53 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 18 |
| Embodied Water, L/kg | 46 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 94 | |
| 33 to 98 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 to 900 | |
| 120 to 300 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 13 to 16 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 10 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0.4 to 0.47 | |
| 0.060 to 0.1 |
| Iron (Fe), % | 98.5 to 99 | |
| 99.245 to 99.67 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.25 to 0.45 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.025 |