SAE-AISI 1046 Steel vs. CC765S Brass
SAE-AISI 1046 steel belongs to the iron alloys classification, while CC765S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1046 steel and the bottom bar is CC765S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 210 | |
| 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 14 to 17 | |
| 21 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 72 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 740 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 370 to 610 | |
| 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 140 |
| Melting Completion (Liquidus), °C | 1460 | |
| 860 |
| Melting Onset (Solidus), °C | 1420 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Conductivity, W/m-K | 51 | |
| 91 |
| Thermal Expansion, µm/m-K | 11 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 34 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 24 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.0 |
| Embodied Energy, MJ/kg | 18 | |
| 51 |
| Embodied Water, L/kg | 46 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 95 | |
| 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 990 | |
| 220 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 23 to 26 | |
| 19 |
| Strength to Weight: Bending, points | 22 to 23 | |
| 18 |
| Thermal Diffusivity, mm2/s | 14 | |
| 28 |
| Thermal Shock Resistance, points | 23 to 25 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.5 to 2.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.080 |
| Carbon (C), % | 0.43 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 51 to 65 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 0.5 to 2.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.5 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0.3 to 3.0 |
| Nickel (Ni), % | 0 | |
| 0 to 6.0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 1.0 |
| Zinc (Zn), % | 0 | |
| 19.8 to 47.7 |