SAE-AISI 1064 Steel vs. C48600 Brass
SAE-AISI 1064 steel belongs to the iron alloys classification, while C48600 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1064 steel and the bottom bar is C48600 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 12 to 13 | |
| 20 to 25 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 72 | |
| 39 |
| Shear Strength, MPa | 430 to 440 | |
| 180 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 730 | |
| 280 to 360 |
| Tensile Strength: Yield (Proof), MPa | 470 to 480 | |
| 110 to 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 120 |
| Melting Completion (Liquidus), °C | 1460 | |
| 900 |
| Melting Onset (Solidus), °C | 1420 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 51 | |
| 110 |
| Thermal Expansion, µm/m-K | 11 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 28 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 24 |
| Density, g/cm3 | 7.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 19 | |
| 47 |
| Embodied Water, L/kg | 46 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 to 81 | |
| 55 to 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 630 | |
| 61 to 140 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 25 to 26 | |
| 9.5 to 12 |
| Strength to Weight: Bending, points | 23 | |
| 12 to 14 |
| Thermal Diffusivity, mm2/s | 14 | |
| 36 |
| Thermal Shock Resistance, points | 25 | |
| 9.3 to 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Arsenic (As), % | 0 | |
| 0.020 to 0.25 |
| Carbon (C), % | 0.6 to 0.7 | |
| 0 |
| Copper (Cu), % | 0 | |
| 59 to 62 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 0 |
| Lead (Pb), % | 0 | |
| 1.0 to 2.5 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.3 to 1.5 |
| Zinc (Zn), % | 0 | |
| 33.4 to 39.7 |
| Residuals, % | 0 | |
| 0 to 0.4 |