SAE-AISI 1070 Steel vs. EN 1.5525 Steel
Both SAE-AISI 1070 steel and EN 1.5525 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is SAE-AISI 1070 steel and the bottom bar is EN 1.5525 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 230 | |
| 130 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 10 to 13 | |
| 11 to 21 |
| Fatigue Strength, MPa | 270 to 350 | |
| 210 to 310 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 34 to 51 | |
| 62 to 73 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 380 to 460 | |
| 310 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 760 | |
| 440 to 1440 |
| Tensile Strength: Yield (Proof), MPa | 420 to 560 | |
| 300 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 50 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 46 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 to 86 | |
| 44 to 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 470 to 850 | |
| 240 to 640 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 27 | |
| 16 to 51 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 16 to 36 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 21 to 25 | |
| 13 to 42 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.65 to 0.75 | |
| 0.18 to 0.23 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 98.3 to 98.8 | |
| 97.7 to 98.9 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.9 to 1.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.025 |