SAE-AISI 1070 Steel vs. C69300 Brass
SAE-AISI 1070 steel belongs to the iron alloys classification, while C69300 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1070 steel and the bottom bar is C69300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 10 to 13 | |
| 8.5 to 15 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 72 | |
| 41 |
| Shear Strength, MPa | 380 to 460 | |
| 330 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 760 | |
| 550 to 630 |
| Tensile Strength: Yield (Proof), MPa | 420 to 560 | |
| 300 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 160 |
| Melting Completion (Liquidus), °C | 1460 | |
| 880 |
| Melting Onset (Solidus), °C | 1420 | |
| 860 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Conductivity, W/m-K | 50 | |
| 38 |
| Thermal Expansion, µm/m-K | 12 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 26 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 19 | |
| 45 |
| Embodied Water, L/kg | 46 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 59 to 86 | |
| 47 to 70 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 470 to 850 | |
| 400 to 700 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 23 to 27 | |
| 19 to 21 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 21 to 25 | |
| 19 to 22 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.65 to 0.75 | |
| 0 |
| Copper (Cu), % | 0 | |
| 73 to 77 |
| Iron (Fe), % | 98.3 to 98.8 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.090 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0.040 to 0.15 |
| Silicon (Si), % | 0 | |
| 2.7 to 3.4 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 18.4 to 24.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |